Welcome to the Piano World Piano Forums Over 3 million posts about pianos, digital pianos, and all types of keyboard instruments. Over 100,000 members from around the world.
Join the World's Largest Community of Piano Lovers
(it's free)
It's Fun to Play the Piano ... Please Pass It On!
|
|
66 members (bobrunyan, anotherscott, AaronSF, apianostudent, beeboss, brdwyguy, benkeys, 15 invisible),
2,196
guests, and
389
robots. |
Key:
Admin,
Global Mod,
Mod
|
|
|
Joined: May 2006
Posts: 14
Junior Member
|
OP
Junior Member
Joined: May 2006
Posts: 14 |
Replacing p.block in Steinert grand, which kind do you recommend? Should I go with the fewer-ply rock maple, or the very-many-ply Euro beech? Which brand carries the best reputation for longevity, etc. ? This year Steinert has nearly parallel bass pins which increase the stresses there a little more than another piano, so I am looking for your opinions as to the "strongest" block available. Thanks, Peter
|
|
|
|
Joined: Jun 2006
Posts: 1,740
1000 Post Club Member
|
1000 Post Club Member
Joined: Jun 2006
Posts: 1,740 |
I've used Bolduc pinblocks with excellent results. They are of the fewer-ply rock maple quarter-sawn. I think he is amongst the most expensive, but you get wht you par for. www.pianobolduc.com/index.html
|
|
|
|
Joined: Dec 2003
Posts: 788
500 Post Club Member
|
500 Post Club Member
Joined: Dec 2003
Posts: 788 |
If you are primarily interested in strength and longevity, use either a Delignit or Falconwood block. They are denser and stronger. Be warned that they are also harder to control. The reason that people don't always use them is that there is very little room for error when drilling. They are so dense that even small variances in drilling can produce uneven results. There are ways of dealing with this. What I do is to drill the block in two passes. When drilling for 2/0 pins, the first pass is with a .250 bit. Then I go through with the final bit. This last bit basically just skims the surface of the hole. This way the bit doesn't overheat, and it gives a more consistent feel to the pins. I also sort the pins. Depending on the brand of tuning pins you buy, there can be a good bit of variance in the diameter. I find that it is worth it to buy the more expensive pins. They are more consistent. Again, with a dense block, this makes more of a difference in the feel of the tuning pins when you are done.
|
|
|
|
Joined: Mar 2005
Posts: 2,726
2000 Post Club Member
|
2000 Post Club Member
Joined: Mar 2005
Posts: 2,726 |
My re-builder has used nothing but Falconwood pinblocks for the last 20+ years. Every Falconwood he has installed has NEVER failed, and they are all still working properly. That has to say something about the quality. He also mentioned to me how important the drilling was and how the bit should be new etc.
|
|
|
|
Joined: May 2006
Posts: 14
Junior Member
|
OP
Junior Member
Joined: May 2006
Posts: 14 |
Thanks for the input. I agree with the double-pass drilling regardless of block type/brand. The Steinert, being a close copy of the Steinway, originally had the fewer-ply rock-maple so I am leaning that way. I guess I am leary anyway about 20+ plys in 1 1/2"s. In drum-building, plywood shells are quite dead compared to the solid wood ones (stave construction for example). It's the high glue content that doesn't allow the shell to ring, only "thud" because the glue is softer than the wood. In a pinblock, I am wondering if it makes any difference ... Anyway, thanks again!
|
|
|
|
Joined: Dec 2003
Posts: 788
500 Post Club Member
|
500 Post Club Member
Joined: Dec 2003
Posts: 788 |
I have never heard of anyone using this criteria to select a pinblock. Maybe I've lived a sheltered life? Maybe we are going to start to hear stories of technicians who select pinblocks by thumping them and seeing which has the best ringtime
|
|
|
|
Joined: Jun 2003
Posts: 32,060
Yikes! 10000 Post Club Member
|
Yikes! 10000 Post Club Member
Joined: Jun 2003
Posts: 32,060 |
I think the maple that was used in old American pianos is a bit better for pinblocks than the beech that was used in old European pianos. But for the most part, it does not matter that much.
Semipro Tech
|
|
|
|
Joined: May 2006
Posts: 14
Junior Member
|
OP
Junior Member
Joined: May 2006
Posts: 14 |
RoyP, It certainly depends on which "glue" is used. I am, however, persuaded that with any project which relies upon the abilities of wood to perform some function, there is (for concise purposes) a wood/glue ratio limit that must not be approached so as not to diminish the effect desired from the wood. There are, obviously, very rich results to be had by the synergistic use of wood and epoxies but we must play by the rules to get the best possible results from the two. For the current piano in question, I am very interested in squeezing out the last bit of performance from the best designed and built pinblock (because of the inherent increased strains placed upon it from the bass string pin pattern. And, for kicks, I probably WILL tap the block when I get it just to see how it sounds, now that you mention it!
|
|
|
|
Joined: Jan 2007
Posts: 115
Full Member
|
Full Member
Joined: Jan 2007
Posts: 115 |
I use rock maple.How old is the Steinert pin block? how loose were the pins and their size? the reason for these questions are that that pin block was designed for that bass for a reason. I try to replace the pin block with the same one that came out or the closest as posible.It wont hurt to go to an twelve ply or more and the glue factor is important.Does the original pin block have any delaminations or cracks in the wood between the glue layers,this can also help you decide which way to go.More layers of pinblock could posibly eliminate cracking.Less layers could posibly eliminate delaminations.Also the conditions the piano was in has a big barring on this to. I travel through maine to Monson a few times a year.Cold winters tend to dry out Pin blocks,especialy when wood stoves are blasting out the heat.If this is the case with this piano I would use Falconwood and double drill.I also use a brass wire cleaning rod ,the same used in cleaning my 22 rifle barrel.It rufes up the wood inside the hole and takes out any glue that may have solidified from the heat build up of the drilling.Sory to go so long with this,but getting it right the first time is very important and costly if done wrong.
Jeffrey T. Swensen 35 years doing restorations Tuning,Moving,Actions,Refinishing, Restringing, Estimates,Players jeffreyswensen@comcast.net
|
|
|
|
Joined: Jun 2001
Posts: 4,864
4000 Post Club Member
|
4000 Post Club Member
Joined: Jun 2001
Posts: 4,864 |
Is is really better to double drill? I've always used a new bit with each block, and air-cooled it while drilling. Worked fine for me. I'll bet most makers don't double drill.
|
|
|
|
Joined: May 2004
Posts: 2,018
2000 Post Club Member
|
2000 Post Club Member
Joined: May 2004
Posts: 2,018 |
The pinblock is structural and some people go to great lengths to dampen noise coing from parts of the piano other than the soundboard and strings. For stabilty you are better of with more laminations.
Hey Steinert- I'm going to be gluing up my first board (or drum head as I think of it) on Monday and I would like to know what glue you think has the best sound transmission. That will be the ribs on monday and the board in the piano on Wednesday
Keith Roberts Keith's Piano Service Hathaway Pines,Ca
|
|
|
|
Joined: May 2006
Posts: 14
Junior Member
|
OP
Junior Member
Joined: May 2006
Posts: 14 |
Keith, Well, honestly I actually have scratched my head many times regarding the glueing of the ribs to the soundboard. Glueing the grain of the ribs at 90 degrees to the grain of the soundboard requires some guts I should think, ... but all pianos are thus made! I realize that with movement of the wood, the board has several options to deal with the strain, but I still can't get over my "feeling" that it just shouldn't work as well as it does ( it's not many-ply, there is such a small cross-sectional mating surface across the rib and such a long surface in the direction of the rib. Like a metal bi-layer switch, the board can still move, but there's a lot of strain and I would be afraid of putting an epoxy that is too hard/brittle, even though that would have better sound transmission than something soft ... but if those ribs delaminate then where's the sound transmission now? With a history in boatbuilding, I typically use the WestSystem epoxies anyway, and just keep the layer of glue real thin where ever I am in the piano
|
|
|
|
Joined: Apr 2005
Posts: 3,203
3000 Post Club Member
|
3000 Post Club Member
Joined: Apr 2005
Posts: 3,203 |
I beleive I have video of the M&H factory drilling, taken last year ... will post a link later when I get home ...
|
|
|
|
Joined: May 2006
Posts: 14
Junior Member
|
OP
Junior Member
Joined: May 2006
Posts: 14 |
Jeff, I am guessing the pinblock is original (because it is the fewer-ply, rock maple type) which would be roughly 85 years old. It has no delamination showing, but much checking! This piano had several drinks spilled into from what I understand (I know nothing about mixed drinks, but it looks like milk-shakes were spilled by the look of the old crud I had to chisel off the soundboard on one side!!. The piano came from Colorado, so I thought it would swell like crazy coming to the coast of Maine, but your right, I haven't had to do much to dry out the soundboard this winter. The pinblock was already all cracked up before it dried out. If I put the new pinblock in a kiln and bring it down to 8% EMC, then install, this winter (so it doesn't swell too much before I get fitted and installed) I shouldn't have any further problems with dry winters. I would like to use the rock maple, but I prefer "right" to "want!"
|
|
|
|
Joined: Apr 2005
Posts: 3,203
3000 Post Club Member
|
3000 Post Club Member
Joined: Apr 2005
Posts: 3,203 |
here's drilling be done at the M&H factory last year on the PW Tour M&H Drilling
|
|
|
|
Joined: Oct 2004
Posts: 2,456
2000 Post Club Member
|
2000 Post Club Member
Joined: Oct 2004
Posts: 2,456 |
Steinert Fan
I don't recommend drying the pin block down.
A properly drilled Maple pin block like Boldoc or Steinway has such a fabulous feel to tune.
As it is pointed out here by other posters, delignit, falcon wood, excalibur are all excellent when drilled properly. And they are drilled a little differently.
Delignit and Falconwood are particularly sensitive to tighter tolerances when drilling.
Tapping the pin block will not yield anything useful towards the sound of the piano.
Tolerances for bearing, sound board design, execution of the installation, string scale design, understanding actions, best hammers for your desired sound, execution of the action work ... are all critical to the outcome.
I can't stress enough getting involved with some of the PTG folks in Maine and there are some good techs there.
If you don't mind me asking, where in Maine are you?
Larry
|
|
|
|
Joined: May 2006
Posts: 14
Junior Member
|
OP
Junior Member
Joined: May 2006
Posts: 14 |
Larry, I didn't mean that I would tap the pinblock as to determine what usefulness it might be for the finished piano's sound; during the short discourse on glue/wood combos as applied to various projects, I only meant that the ratios and types would effect the job required of it, which I agree is NOT sound amplification! I did mention I that I would probably rap on it after the discussion, but that's for kicks, not actually experimentation toward imroving anything sound-wise (I tap on a lot of stuff: trees, shovels, kitchen table, ... my own head! I am a curious kid first, then a musician, then a piano player, and then a piano tinkerer!) As I thought about it, I have to agree with not drying the block. As mentioned earlier, just trying to sqeeze out the most strength and stability from a new pinblock since the design of this Steinert has a reputation for being hard on pinblocks (parallel bass pins). Thanks for the info.
|
|
|
|
Joined: Oct 2004
Posts: 2,456
2000 Post Club Member
|
2000 Post Club Member
Joined: Oct 2004
Posts: 2,456 |
The amount and placement of end grain wood relative to the force on the pin, the fit of the block to the plate flange and webbing are primary. Assuming a well made block ...
The orientation of the bass pins in the Steinert is not serious if all else is well.
If all else is NOT well, than ANY orientation of pins will not work. The stress of the string tension will cause failure.
Over the years it is easy to see how the actual way pin blocks are laid up as being the significant cause of failures, right next to bad environments .....
Pianos such as the Mason and Hamlin A(older ones, not sure about todays Mason A) has a very small profile of block in the bass and more care in fitting is necessary there to support the section adequately.
I have a Knabe in my shop right now where the pins in the tenor section are right next to the flange. Very little wood for support. I am looking that one over carefully.
BTW, where in Maine did you say you were?
Boston and NH have a lot of good speakers coming this spring. Many of the Maine folks are attending.
Larry
|
|
|
|
Joined: May 2004
Posts: 2,018
2000 Post Club Member
|
2000 Post Club Member
Joined: May 2004
Posts: 2,018 |
Ribs have to be glued at 90* to the grain. It's structural. Plywood across joists is the same.
If you picked up a board glued with the grain along the ribs, it would snap in half. The flex of the compression crown would cause the board to bubble or be wavy between ribs. The board would not have the stiffness.
Keith Roberts Keith's Piano Service Hathaway Pines,Ca
|
|
|
|
Joined: May 2006
Posts: 14
Junior Member
|
OP
Junior Member
Joined: May 2006
Posts: 14 |
Keith, Yes, of course, everything is designed accordingly, it would be foolish to stray from that design. I simply can't get past the idea that a rib spanning that much width of the soundboard, across the grain, doesn't come loose more often with changes in humidity. As the board flexes with the changes, even though both the ribs and the board move, still there has to be either some sliding that must take place between the rib and the board or the rib must compress tremendously. Knowing how much tension there is from the strings I know it is very possible to compress spruce along the grain that much, but it just doesn't feel right under my skin. I am not negating what is the clear and proven method employed for hundreds of years, I was just expressing my lack of comfort with it. In my mind, all the ribs would buckle loose every spring if not every fall ... but clearly that's not the reality!
|
|
|
|
|
|
Piano
by Gino2 - 04/17/24 02:34 PM
|
Piano
by Gino2 - 04/17/24 02:23 PM
|
|
Forums43
Topics223,408
Posts3,349,457
Members111,637
|
Most Online15,252 Mar 21st, 2010
|
|
|
|
|
|